Singlemode Fiber- G.657A3 Wasin Fujikura
Nanjing Wasin Fujikura G.657A3 singlemode fiber hawwe minimum bûgen characterstic.satisfied oerdracht eask yn komplekse omjouwing benammen yn 1310nm en 1550nm wurkje goed, kin brûkt wurde tegearre mei oare G657.
optreden
| karakteristyk | betingst | datum | ienheid | |
| Optyske spesifikaasjes | ||||
| Attenuation koëffisjint | 1310 nm 1383 nm 1550 nm 1625 nm |
≤0.35 ≤0.34≤0.21 ≤0.24 | dB/kmdB/kmdB/km dB/km |
|
| Attenuation vs.Wavelength | @1310nm@1550nm | 1285~1330nm1525~1575 nm | ≤0.04≤0.03 | dB/kmdB/km |
| Wavelenth Dispersion | 1285~1340nm1550nm~1625nm1625nm | ≤18≤22 | ps / (nm·km)ps / (nm·km) | |
| Zero-dispersion golflingte | 1300~1324 | nm | ||
| Zero-dispersion helling | ≤0,092 | ps/(nm2·km) | ||
| Polarisaasjemodus fersprieding PMDSInkelfiber maksimale weardeFiberlinkwearde (M=20, Q=0.01%) | ≤0.20≤0.10 | ps/√kmps/√km | ||
| kabel cutoff golflingte | ≤1260 | nm | ||
| Mode fjild diameter MFD | 1310 nm | 8,6±0,4 | μm | |
| Punt diskontinuïteit | 1550 nm | ≤0,05 | dB | |
| Ofmjittings prestaasjes | ||||
| Bekleding diameter | 125±0,7 | μm | ||
| Cladding Non-circularity | ≤0.5 | % | ||
| Outer coating diameter | 245±10 | μm | ||
| Beklaaiïng / Coating Concentricity | ≤12,0 | μm | ||
| Core / beklaaiïng konsintrisiteit | ≤0.5 | μm | ||
| kromte (radius) | 24 | m | ||
| lingte | 2.0~50.4 | km/rol | ||
| Miljeuprestaasjes (1310nm/1550nm) | ||||
| Fochtige waarmte | 85 ℃, Feuchte ≥ 85%, 30 dagen | ≤0,05 | dB/km | |
| Droege waarmte | 85 ℃ ± 2 ℃, 30 dagen | ≤0,05 | dB/km | |
| Temperatuer ôfhinklikens | -60℃ ~ +85℃, twa wiken | ≤0,05 | dB/km | |
| Water immersion | 23 ℃ ± 5 ℃, 30 dagen | ≤0,05 | dB/km | |
| Meganyske prestaasjes | ||||
| Bewiis testnivo | ≥0,69 | GPa | ||
| Macrobend ferlies 10 draaienφ30mm1 draaienφ20mm1 draaienφ20mm 1 draait φ15 mm 1 draait φ15 mm 1 draait φ10 mm 1 omt10mm |
1550 nm1625 nm
1550 nm 1625 nm 1550 nm 1652nm |
≤0.03≤0.1 ≤0,08 ≤0,25 ≤0,15 ≤0,45 |
dBdB dB dB dB dB |
|
| Strip krêft | 1.0~5.0 | N | ||
| Dynamic fatigue parameter | ≥20 | |||
Skriuw jo berjocht hjir en stjoer it nei ús